PA6 G9HT K01
40% glass fiber reinforced
Thermal stability rating
Material Technical Datasheet | ||||
PA6 G9HT K01 | ||||
Material Properties | ||||
40% glass fiber reinforced thermal stability rating | ||||
FEATURES | APPLICATIONS | |||
Good appearance | Automotive hood | |||
Dimensional stability | Automotive components | |||
High strength | Injection molding applications | |||
Physical Properties | ||||
Properties | Test Standard | Test Condition | Units | Data |
Specific Gravity | ISO 1183 | 23°C | g/cm³ | 1.51 |
Shrinkage Rate | ISO 2577 | flow | % | 0.2 |
Shrinkage Rate | ISO 2577 | perpendicular | % | 0.8 |
Water absorption rate | ISO 62 | 23 ° C 50RH balance | % | 1.2 |
Ash content | ISO 3451 | % | 45 | |
Mechanical Properties | ||||
Mechanical Properties | Test Standard | Test Condition | Units | Data |
Tensile Strength | ISO 527 | 1.0mm/min | Mpa | 11000 |
Elongation at Break | ISO 527 | 5mm/min | % | 190 |
Flexural Strength | ISO 178 | 2.0mm/min | Mpa | 290 |
Flexural Modulus | ISO 178 | 2.0mm/min | Mpa | 10000 |
Thermal Properties | ||||
Thermal Properties | Test Standard | Test Condition | Units | Data |
Thermal deformation temperature | ISO 75 | 0.45MPa | ℃ | 220 |
Thermal deformation temperature | ISO 75 | 1.8MPa | ℃ | 205 |
Electrical Performance | ||||
Electrical Performance | Test Standard | Data | Units | |
Volume resistance | IEC 60093 | 1.00E+15 | Ω.cm | |
Flame Retardancy | ||||
Flame Retardancy | Test Standard | Data | ||
Fire Rating 1.6mm | UL94 | HB | ||
Injection Molding | ||||
Injection Molding | Units | Data | ||
Drying Temperature | ℃ | 90~120 | ||
Drying Time | h | 4~6 | ||
Front Temperature | ℃ | 230~250 | ||
Middle Temperature | ℃ | 250~270 | ||
Temperature of The Third Section | ℃ | 250~280 | ||
Melting temperature | ℃ | 255~280 | ||
Maximum melting temperature | ℃ | 300 | ||
Mold Temperature | ℃ | 50~70 | ||
Injection speed | High speed | |||
Injection speed | High speed |