PA6 G4 K01
20% glass fiber reinforced
Material Technical Datasheet | ||||
PA6 G4 K01 | ||||
Material Properties | ||||
20% glass fiber reinforced | ||||
FEATURES | APPLICATIONS | |||
Good appearance | Home appliance applications | |||
Dimensional stability | Electric tool handle | |||
Good mechanical performance | Sports Goods Application |
|||
Injection molding applications | ||||
Properties | Test Standard | Test Condition | Units | Typical Values |
Physical Properties | ||||
Specific Gravity | ISO 1183 | 23°C | g/cm³ | 1.28 |
Shrinkage Rate | ISO 2577 | flow | % | 0.5 |
Shrinkage Rate | ISO 2577 | perpendicular | % | 1 |
Water absorption rate | ISO 62 | 23 ° C 50RH balance | % | 2.2 |
Ash content | ISO 3451 | % | 20 | |
Mechanical Properties | ||||
Mechanical Properties | Test Standard | Test Condition | Units | Data |
Tensile Strength | ISO 527 | 23 ° C 10mm/min | Mpa | 145 |
Elongation at Break | ISO 527 | 23 ° C 10mm/min | % | 3.3 |
Flexural Strength | ISO 178 | 23 ° C 2.0mm/min | Mpa | 215 |
Flexural Modulus | ISO 178 | 23 ° C 2.0mm/min | Mpa | 6200 |
Cantilever beam notch impact | ISO 180 | 23 ° C | kJ/m2 | 12 |
Thermal Properties | ||||
Thermal Properties | Test Standard | Test Condition | Units | Data |
Thermal deformation temperature | ISO 75 | 0.45MPa | ℃ | 215 |
Thermal deformation temperature | ISO 75 | 1.8MPa | ℃ | 205 |
Electrical Performance | ||||
Electrical Performance | Test Standard | Data | Units | |
Volume resistance | IEC 60093 | 1.51E+3 | Ω.cm | |
Flame Retardancy | ||||
Flame Retardancy | Test Standard | Data | ||
Fire Rating | UL94 | HB | ||
Injection Molding | ||||
Injection Molding | Units | Data | ||
Drying Temperature | ℃ | 90~110 | ||
Drying Time | h | 4~6 | ||
Front Temperature | ℃ | 230~250 | ||
Middle Temperature | ℃ | 250~270 | ||
Temperature of The Third Section | ℃ | 260~280 | ||
Melting temperature | ℃ | 255~280 | ||
Maximum melting temperature | ℃ | 300 | ||
Mold Temperature | ℃ | 50~120 | ||
Injection speed | High speed |