PA6 G5HT K01
25% glass fiber reinforced, thermally stable and graded
description1
Zipper closure
1/5 zip athletic pullovers for men. Stretchy, lightweight, fast-drying
fabric for superior performance.
REGULAR FIT - US standard sizes. An athletic fit that sits close to the
body
for a wide range of motion, designed for optimal performance and all day
comfort.
FEATURES - Quarter zip closure;Thumbholes on long sleeves to keep them
in
place during workout
Information
| Material Technical Datasheet | ||||
| PA6 G5HT K01 | ||||
| Material Properties | ||||
| 25% glass fiber reinforced, thermally stable and graded | ||||
| FEATURES | APPLICATIONS | |||
| Good appearance | Automotive hood | |||
| Dimensional stability | Automotive components | |||
| High strength | Injection molding applications |
|||
| Physical Properties | ||||
| Properties | Test Standard | Test Condition | Units | Data |
| Specific Gravity | ISO 1183 | 23°C | g/cm³ | 1.32 |
| Shrinkage Rate | ISO 2577 | flow | % | 0.3 |
| Shrinkage Rate | ISO 2577 | perpendicular | % | 1 |
| Water absorption rate | ISO 62 | 23 ° C 50RH balance | % | 2.3 |
| Ash content | ISO 3451 | % | 25 | |
| Mechanical Properties | ||||
| Mechanical Properties | Test Standard | Test Condition | Units | Data |
| Tensile Strength | ISO 527 | 1.0mm/min | Mpa | 8000 |
| Elongation at Break | ISO 527 | 5mm/min | % | 155 |
| Flexural Strength | ISO 178 | 2.0mm/min | Mpa | 220 |
| Flexural Modulus | ISO 178 | 2.0mm/min | Mpa | 7000 |
| Thermal Properties | ||||
| Thermal Properties | Test Standard | Test Condition | Units | Data |
| Thermal deformation temperature | ISO 75 | 0.45MPa | ℃ | 220 |
| Thermal deformation temperature | ISO 75 | 1.8MPa | ℃ | 200 |
| Electrical Performance | ||||
| Electrical Performance | Test Standard | Data | Units | |
| Volume resistance | IEC 60093 | 1E15 | Ω.cm | |
| Flame Retardancy | ||||
| Flame Retardancy | Test Standard | Data | ||
| Fire Rating | UL94 | HB | ||
| Injection Molding | ||||
| Injection Molding | Units | Data | ||
| Drying Temperature | ℃ | 100～130 | ||
| Drying Time | h | 4～6 | ||
| Front Temperature | ℃ | 230～250 | ||
| Middle Temperature | ℃ | 250～270 | ||
| Temperature of The Third Section | ℃ | 250～280 | ||
| Melting temperature | ℃ | 255~280 | ||
| Maximum melting temperature | ℃ | 300 | ||
| Mold Temperature | ℃ | 50～120 | ||
| Injection speed | High speed | |||