Home  >  Products  >  PP Compound  >  PP HT K03

Products

description1
Zipper closure 1/5 zip athletic pullovers for men. Stretchy, lightweight, fast-drying fabric for superior performance. REGULAR FIT - US standard sizes. An athletic fit that sits close to the body for a wide range of motion, designed for optimal performance and all day comfort. FEATURES - Quarter zip closure;Thumbholes on long sleeves to keep them in place during workout
Information
Material Technical Datasheet
PP HT K03
 PROPERTY
High heat resistance grade
FEATURES APPLICATIONS
Low shrinkage and high impact  Home appliance components
High rigidity and low warpage  Injection molding application
High temperature resistance  
Properties Test Standard Test Condition Units Typical Values
Physical Properties
Specific Gravity ISO 1183 23℃ g/cm³ 1.03
Shrinkage Rate ISO 2577 23℃ % 0.5~0.9
Melt index 230°C 2.16kg ISO 1133 16 g/10min 6
Mechanical Properties
Mechanical Properties Test Standard Test Condition Units Data
Tensile Strength  ISO 527 10mm/min Mpa 45
Elongation at Break  ISO 527 10mm/min % 6
Flexural Strength  ISO 178 2.0mm/min Mpa 60
Flexural Modulus  ISO 178 2.0mm/min Mpa 2500
Cantilever notch impact  ISO 180 23 ° C A-notch kJ/m² 10
Thermal Properties
Thermal Properties Test Standard Test Condition Units Data
H.D.T  ISO 75 0.45MPa 145
Electrical Performance
Electrical Performance Test Standard Data Units
Volume resistance IEC 60093 1E16 Ω.cm
Flame Retardancy
Flame Retardancy Test Standard Data
Fire Rating Full Color 1.5mm UL94 HB
Fire Rating Full Color 3.3mm UL94 HB
UL
Flame Retardancy Test Standard Data Units
Fire Rating Full Color 1.5mm UL94 HB  
Fire Rating Full Color 3.3mm UL94 HB  
HAI Full Color 1.5mm UL 746A 0 PLC
HAI Full Color 3.3mm UL 746A 0 PLC
RTI Elec Full color 1.5mm UL 746B 65 °C
RTI Elec Full color3.3mm UL 746B 65 °C
RTI Imp Full color 1.5mm UL 746B 65 °C
RTI Imp Full color 3.3mm UL 746B 65 °C
RTI Str Full color 1.5mm UL 746B 65 °C
RTI Str Full color 3.3mm UL 746B 65 °C
Injection Molding
Injection Molding Units Data
Drying Temperature 90
Drying Time h 2
Front Temperature 180~210
Middle Temperature 190~230
Temperature of The Third Section 200~240
Melting temperature 190~245
Maximum melting temperature 260
Mold Temperature 30~100
Injection speed Medium speed
Back pressure KPa 10