PC FRG50 K2
50% glass fiber reinforced
High heat resistance level
Material Technical Datasheet | ||||
PC FRG50 K2 | ||||
Material Properties | 50% glass fiber reinforced High heat resistance level |
|||
FEATURES | APPLICATIONS | |||
Good surface | Electronic and electrical applications | |||
Dimensional stability | CD/DVD internal holder | |||
Good mechanical performance | Internal structure of OA equipment | |||
High rigidity | Imaging device housing | |||
Low warpage | Computer plug | |||
High temperature resistance | Precision molding applications | |||
Properties | Test Standard | Test Condition | Units | Typical Values |
Physical Properties | ||||
Specific Gravity | ISO 1183 | 23℃ | g/cm³ | 1.62 |
Shrinkage Rate | ISO 2577 | % | 0.1~0.3 | |
Ash Content | ISO 3451 | 825°C 40min | % | 50 |
Mechanical Properties | ||||
Mechanical Properties | Test Standard | Test Condition | Units | Data |
Tensile Strength | ISO 527 | 10mm/min | Mpa | 135 |
Elongation at Break | ISO 527 | 10mm/min | % | 4 |
Flexural Strength | ISO 178 | 2.0mm/min | Mpa | 200 |
Flexural Modulus | ISO 178 | 2.0mm/min | Mpa | 12000 |
Cantilever notch impact | ISO 180 | 23°C 4.0mm | J/m2 | 12 |
Cantilever beam impact without notch | ISO 180 | 23°C 4.0mm | J/m2 | 40 |
Thermal Properties | ||||
Thermal Properties | Test Standard | Test Condition | Units | Data |
H.D.T | ISO 75 | 1.8MPa 4.0mm | ℃ | 148 |
Electrical Performance | ||||
Electrical Performance | Test Standard | Data | Units | |
Volume resistance | IEC 60093 | 1E15 | Ω | |
Insulation Strength 1.6mm | IEC 60243 | 22 | KV/mm | |
Flame Retardancy | ||||
Flame Retardancy | Test Standard | Data | ||
Fire Rating Full Color 1.6mm | UL94 | V-2 | ||
Fire Rating Full Color 3.0mm | UL94 | V-2 | ||
UL | ||||
Flame Retardancy | Test Standard | Data | Units | |
Fire Rating Full Color 1.5mm | UL94 | V-2 | ||
Fire Rating Full Color 3.0mm | UL94 | V-2 | ||
RTI Elec 1.6mm | UL 746B | 80 | °C | |
RTI Elec 3.0mm | UL 746B | 80 | °C | |
RTI Imp 1.6mm | UL 746B | 80 | °C | |
RTI Imp 3.0mm | UL 746B | 80 | °C | |
RTI Str 1.6mm | UL 746B | 80 | °C | |
RTI Str 3.0mm | UL 746B | 80 | °C | |
Injection Molding | ||||
Injection Molding | Units | Data | ||
Drying Temperature | ℃ | 110~120 | ||
Drying Time | h | 4~6 | ||
Front Temperature | ℃ | 230~260 | ||
Middle Temperature | ℃ | 240~290 | ||
Temperature of The Third Section | ℃ | 250~320 | ||
Melting temperature | ℃ | 230~320 | ||
Maximum melting temperature | ℃ | 330 | ||
Mold Temperature | ℃ | 80~120 | ||
Injection speed | Medium and low speed |